Magnetic Chitosan Bionanocomposite Films as a Versatile Platform for Biomedical Hyperthermia.

Responsive magnetic nanomaterials offer significant advantages for innovative therapies, for instance, in cancer treatments that exploit on-demand delivery on alternating magnetic field (AMF) stimulus. In this work, biocompatible magnetic bionanocomposite films are fabricated from chitosan by film casting with incorporation of magnetite nanoparticles (MNPs) produced by facile one pot synthesis. The influence of synthesis conditions and MNP concentration on the films' heating efficiency and heat dissipation are evaluated through spatio-temporal mapping of the surface temperature changes by video-thermography. The cast films have a thickness below 100 µm, and upon exposure to AMF (663 kHz, 12.8 kA m-1 ), induce exceptionally strong heating, reaching a maximum temperature increase of 82 °C within 270 s irradiation. Further, it is demonstrated that the films can serve as substrates that supply heat for multiple hyperthermia scenarios, including: i) non-contact automated heating of cell culture medium, ii) heating of gelatine-based hydrogels of different shapes, and iii) killing of cancerous melanoma cells. The films are versatile components for non-contact stimulus with translational potential in multiple biomedical applications.

Magneto-Fluorescent Mesoporous Nanocarriers for the Dual-Delivery of Ofloxacin and Doxorubicin to Tackle Opportunistic Bacterial Infections in Colorectal Cancer.

Cancer-related opportunistic bacterial infections are one major barrier for successful clinical therapies, often correlated to the production of genotoxic factors and higher cancer incidence. Although dual anticancer and antimicrobial therapies are a growing therapeutic fashion, they still fall short when it comes to specific delivery and local action in in vivo systems. Nanoparticles are seen as potential therapeutic vectors, be it by means of their intrinsic antibacterial properties and effective delivery capacity, or by means of their repeatedly reported modulation and maneuverability. Herein we report on the production of a biocompatible, antimicrobial magneto-fluorescent nanosystem (NANO3) for the delivery of a dual doxorubicin-ofloxacin formulation against cancer-related bacterial infections. The drug delivery capacity, rendered by its mesoporous silica matrix, is confirmed by the high loading capacity and stimuli-driven release of both drugs, with preference for tumor-like acidic media. The pH-dependent emission of its surface fluorescent SiQDs, provides an insight into NANO3 surface behavior and pore availability, with the SiQDs working as pore gates. Hyperthermia induces heat generation to febrile temperatures, doubling drug release. NANO3-loaded systems demonstrate significant antimicrobial activity, specifically after the application of hyperthermia conditions. NANO3 structure and antimicrobial properties confirm their potential use in a future dual anticancer and antimicrobial therapeutical vector, due to their drug loading capacity and their surface availability for further modification with bioactive, targeting species.

Assisted Synthesis of Coated Iron Oxide Nanoparticles for Magnetic Hyperthermia.

Magnetite nanoparticles were synthesized by the co-precipitation method with and without the assistance of an additive, namely, gelatin, agar-agar or pectin, using eco-friendly conditions and materials embodying a green synthesis process. X-ray diffraction and transmission electron microscopy were used to analyze the structure and morphology of the nanoparticles. Magnetic properties were investigated by SQUID magnetometry and 57Fe Mössbauer spectroscopy. The results show that the presence of the additives implies a higher reproducibility of the morphological magnetic nanoparticle characteristics compared with synthesis without any additive, with small differences associated with different additives. To assess their potential for magnetic hyperthermia, water-based suspensions of these nanoparticles were prepared with and without citric acid. The stable solutions obtained were studied for their structural, magnetic and heating efficiency properties. The results indicate that the best additive for the stabilization of a water-based emulsion and better heating efficiency is pectin or a combination of pectin and agar-agar, attaining an intrinsic loss power of 3.6 nWg-1.

Coating of Magnetite Nanoparticles with Fucoidan to Enhance Magnetic Hyperthermia Efficiency.

Magnetic nanoparticles (NP), such as magnetite, have been the subject of research for application in the biomedical field, especially in Magnetic Hyperthermia Therapy (MHT), a promising technique for cancer therapy. NP are often coated with different compounds such as natural or synthetic polymers to protect them from oxidation and enhance their colloidal electrostatic stability while maintaining their thermal efficiency. In this work, the synthesis and characterization of magnetite nanoparticles coated with fucoidan, a biopolymer with recognized biocompatibility and antitumoral activity, is reported. The potential application of NP in MHT was evaluated through the assessment of Specific Loss Power (SLP) under an electromagnetic field amplitude of 14.7 kA m-1 and at 276 kHz. For fucoidan-coated NP, it was obtained SLP values of 100 and 156 W/g, corresponding to an Intrinsic Loss Power (ILP) of 1.7 and 2.6 nHm2kg-1, respectively. These values are, in general, higher than the ones reported in the literature for non-coated magnetite NP or coated with other polymers. Furthermore, in vitro assays showed that fucoidan and fucoidan-coated NP are biocompatible. The particle size (between ca. 6 to 12 nm), heating efficiency, and biocompatibility of fucoidan-coated magnetite NP meet the required criteria for MHT application.

Magnetotactic Bacteria: Magnetism Beyond Magnetosomes.

Magnetotactic bacteria are a group of organisms deeply studied in the last years due to their interesting magnetic behavior and potential applications in nanometrology, hyperthermia, and biosensor devices. One intrinsic common characteristic is the presence, inside the bacteria, of magnetic nanoparticles called magnetosomes. The role of magnetosomes as bacterial tools to orient the bacteria and find new habitats is universally accepted, but the way they develop still is not fully understood. A strain of Magnetospirillum magnetotacticum was grown and investigated at the nanoscale using transmission electron microscopy and atomic/magnetic force microscopy techniques. Magnetosomes were observed as well as long filaments with magnetic response that could be associated to the actin-like filaments being crucial to allow the nanoparticles orientation and magnetosomes formation. To the best of our knowledge, this paper is the first to visualize these reproducible long-range size magnetic crystalline structures.